Material Status 

• Commercial: Active

Availability 

Filler / Reinforcement 

• Glass Fiber

Additive 

• Flame Retardant

Features 

Processing Method 

Nominal Value

Unit

Test Method

Density

1.62

g/cm?

Molding Shrinkage

Across Flow

0.60

%

Flow

0.0

%

Nominal Value

Unit

Test Method

Tensile Modulus

17000

MPa

Tensile Stress (Break)

150

MPa

Tensile Strain (Break)

1.5

%

Flexural Modulus (23°C)

16500

MPa

Flexural Stress (23°C)

210

MPa

Nominal Value

Unit

Test Method

Charpy Notched Impact Strength

-30°C

20

kJ/m?

23°C

20

kJ/m?

Charpy Unnotched Impact Strength

-30°C

22

kJ/m?

23°C

30

kJ/m?

Notched Izod Impact Strength (23°C)

18

kJ/m?

Unnotched Izod Impact Strength (23°C)

30

kJ/m?

Nominal Value

Unit

Test Method

Deflection Temperature Under Load (1.8 MPa, Unannealed)

310

°C

Glass Transition Temperature ²

120

°C

Melting Temperature ²

352

°C

CLTE - Flow

3.0E-6

cm/cm/°C

CLTE - Transverse

6.2E-5

cm/cm/°C

Nominal Value

Unit

Test Method

Surface Resistivity (23°C)

> 1.0E+15

ohms

Volume Resistivity (23°C)

> 1.0E+13

ohms·m

Electric Strength ³ (23°C)

45

kV/mm

Dielectric Constant

100 Hz

4.10

1 MHz

3.70

Dissipation Factor

100 Hz

0.014

1 MHz

0.030

Comparative Tracking Index (CTI)

PLC 4

Nominal Value

Unit

Test Method

Flame Rating (0.40 mm)

V-0

Oxygen Index

45

%

Nominal Value

Unit

Drying Temperature

> 150

°C

Drying Time

3.0

hr

Suggested Max Moisture

0.010

%

Hopper Temperature

20 to 30

°C

Injection Feed Temperature

40 to 60

°C

Rear Temperature

355 to 365

°C

Middle Temperature

360 to 370

°C

Front Temperature

360 to 370

°C

Injection Zone 4 Temperature

360 to 370

°C

Nozzle Temperature

360 to 370

°C

Processing (Melt) Temp

360 to 370

°C

Mold Temperature

80 to 120

°C

Injection Pressure

50.0 to 150

MPa

Holding Pressure

50.0 to 150

MPa

Back Pressure

<3.00

MPa